A102 is a stainless steel electrode and cannot be used to weld cast iron.
If you use stainless steel electrode to weld pig iron, it is better to weld pig iron with carbon steel electrode, for example, use J506 structural steel electrode to weld pig iron to preheat the pig iron at about 550 degrees, and put lime pile to keep warm and slow cool after welding. If there is no thermal insulation and slow cooling conditions, the cold welding process is used for welding, and the cold welding process needs to be welded with electrodes suitable for cold welding process welding, such as conventional Z308 electrodes, if it is an important cast iron equipment, the anti-crack requirements are better, and you can also use wewelding777 cast iron electrodes for welding.
Welding specifications. 1. It is necessary to do proper surface cleaning before welding, and the welded joint should be obliquely cut into a U-shaped groove.
2. Crack holes at both ends of the crack to prevent the expansion of the crack during the welding process.
3. When the repair angle is not good, you can choose the wewelding100 electrode cold slotting to form an effective U-shaped or V-shaped groove.
4. Weld with as little current as possible, medium arc length, and slightly inclined to the welding direction.
5. It is recommended that the weld bead should be short, thin and narrow transversely oscillating torch to fill the weld before stopping the arc welding, usually without heat treatment, allowing the parts to cool slowly.
-
Stainless steel electrode Carbon steel electrode cannot weld cast iron, because cast iron is afraid of high temperatures, and you use stainless steel electrodes to weld will definitely make the cast iron crack at high temperatures. Cast iron special welding electrodes can be used. For more information, please see what I know, and call by yourself.
-
Abstract 208 electrode is used to repair the defects of gray cast iron, 208 is a cast iron electrode with low carbon steel core and strong graphitized coating, and the weld can be turned into gray cast iron when it is slowly cooled, and the crack resistance is poor. It can be used for both AC and DC, and the electrode must be baked for about 150 hours before inexpensive welding. For important casting structures such as stress and impact, this electrode should not be used.
The defects of the small thin-walled castings with low stiffness can be welded without preheating, while the general weldments need to be preheated to 400, and the insulation and cooling after welding are slow, and the welding repair may be cut.
Whether the cast iron electrode 208 can weld steel plates and iron castings.
208 electrode is used to weld and repair the defects of gray cast iron, 208 is a cast iron electrode with low carbon steel core and strong graphitized coating, and the weld can be turned into gray cast iron when it is slowly cooled, and the crack resistance is poor. It can be used for both AC and DC, and the electrode must be baked for about 150 hours before inexpensive welding. For important casting structures such as stress and impact, this electrode should not be used.
The defects of the small thin-walled castings with low stiffness can be welded without preheating, while the general weldments need to be preheated to 400, and the insulation and cooling after welding are slow, and the welding repair may be cut.
What kind of electrode can weld cast iron and steel plate?
What kind of electrode can weld the connection gap between cast iron and steel plate?
-
Summary. If you must use a welding rod to weld iron, we can use J506 welding rod for welding, which is also a process method of heat welding, for the shaft iron workpiece to do about 500 degrees of processing after welding, the follow-up needs to do some thermal insulation treatment, so that the success rate of the sub will be higher, in addition, it is also recommended that you use high crack resistance W1777 special boat electrode for welding, or use the method of cold welding for welding, so that the success rate of the shaft welded out will be relatively high.
1. Stainless steel electrode can not be welded cast iron, but pig iron can be welded, because its bearing capacity can not reach the original structure, so it may also need to be heated, if not heated, it is likely to produce cracks in the later stage, but it is not guaranteed that there will be no cracks after processing, so pig iron can be welded.
2. Stainless steel electrodes cannot be used because they are very easy to harden after welding, and they are also prone to cracks, which cannot have a good connection effect. After heating, it will harden, and cracks will appear when it is lifted, and such a fold cannot be used.
If you must use a welding rod to weld iron, we can use J506 welding rod for welding, which is also a process method of heat welding, for the shaft iron workpiece to do about 500 degrees of processing after welding, the follow-up needs to do some thermal insulation treatment, so that the success rate of the sub will be higher, in addition, it is also recommended that you use high crack resistance W1777 special boat electrode for welding, or use the method of cold welding for welding, so that the success rate of the shaft welded out will be relatively high.
If you are satisfied with my service, please give a thumbs up and wish you all the best!
-
Summary. J502 is a titanium-calcium coating, the alloy composition contains nickel, molybdenum and other materials, the toughness of the weld is better, and the weld should be less likely to crack.
J502 is a titanium-calcium coating, the alloy composition contains nickel, molybdenum and other materials, the toughness of the weld is better, and the weld should be less likely to crack.
Unhappy. The carbon content of steel castings is relatively high, and the wewelding600 alloy steel electrode with better crack resistance can be selected to prevent cracks, and the tensile strength after welding is 860MPa, which is higher than that of general carbon steel and steel castings, so the welding of stressed parts is very large, and wewelding600 is still preferred for welding in special crack resistance parts and high-strength parts, because it has good crack resistance, so the welded cast steel can be welded directly by cold welding process, eliminating the complex heat treatment process. Characteristics of WeWelding 600 Special Alloy Steel Electrode Wewelding 600 Alloy Steel Electrode (referred to as Weodin 600 Electrode) is a special nickel-chromium alloy steel electrode with low heat output and suitable for all-round welding, with a wide range of versatility, high strength general base metal strength design, excellent welding process performance, stable arc, uniform and beautiful weld, excellent welding effect under the conditions of oil, water and rust, and can weld different steels.
This is my answer, I hope it is helpful to you, thank you <>
-
102 is a titanium-calcium coated stainless steel electrode。This 102 electrode adopts foreign advanced technology, the electrode coating is red, has good mechanical properties and metal corrosion resistance to the weld metal, and the arc is soft, the spatter is small, and the electrode is not easy to turn red. 2. What are the functions of the welding rod 1. Improve the stability of arc combustion.
The coated electrode is not prone to arcing and does not burn stably even if ignited. 2. In the process of welding loss, the oxygen and nitrogen in the air will adversely affect the weld, reduce the mechanical properties of the weld, lead to cracks, produce a large amount of gas to cover the arc and the weld pool, and reduce the interaction between the molten metal and the air. 3. Ensure that although the deoxidation of the weld has a protective effect during the welding process, it is inevitable that a small amount of oxygen will enter the molten pool, resulting in the oxidation of metal elements and reducing the quality of the weld.
Therefore, in welding, a reducing agent needs to be added to reduce the oxides that have entered the molten pool. 4. Supplement the weld with alloying elements. Welding rods can add alloying elements to the weld to ensure the mechanical properties of the weld, but some alloy steels need to penetrate through the sock seam of the weld to make the metal close to the base metal composition.
5. Improve welding productivity Welding rod can improve welding productivity, and at the same time, it can also reduce the metal loss caused by spatter and improve the deposition coefficient, so as to improve the yield of welded raw car.
-
No. 20 belongs to high-quality low-carbon steel, and ordinary welding rods can do it.
-
The 20 of No. 20 steel refers to the carbon content, and the carbon content is, which belongs to low-carbon steel. Steel can be divided into low carbon steel, medium carbon steel and high carbon steel.
Carbon content: low carbon steel is generally less than; Medium carbon steel is generally between; High-carbon steels are generally greater than.
In addition to containing carbon (C) elements and a certain amount of silicon (Si) for deoxidation (generally not exceeding, manganese (mn) (generally not exceeding, higher can be up to alloying elements), no other alloying elements (except for residual elements).
No. 20 steel can use ordinary welding rods. It can be welded with J422, J427, J507 and can also be welded with gas shielded welding. J507, J427 are welded by reverse connection method, etc.
If the strength grade of the welded material is different for steel pipes, the welding rod can be selected according to the steel grade with the lower strength grade.
-
What welding rod pro is used for white steel 2205 and 20 steel! Hello to you, happy to answer for you. White steel 2205 and No. 20 steel can be welded with E2209 electrode, or you can choose ER2209 welding wire for weldingWhite steel 2205 itself belongs to duplex stainless steel, and welding rods are often needed to weld when connecting
4, or yes. 2205 white steel can be used as a pressure vessel, a high-pressure storage tank, or a high-pressure pipeline, but it can not be integrated during processing, at this time, it is necessary to use E2209 welding rod for processing and forming, especially as an oil and gas pipeline, high-pressure pipeline and sewage treatment pipeline, etc., in the elbow transfer position, must be welded with a welding rod to ensure the sealing, corrosion resistance, and strength of the joint position. I hope my reply to Zheng Cong can help you!
Do you have any other questions?
when dealing ..This is a present participle used as an adverbial. And still"Hanging participle"。 >>>More
Learn electrochemical energy storage and conversion technology; Renewable energy (solar, wind, biomass, ocean, etc.) >>>More
After the new version of the iOS system comes out, Apple will close the system verification of the old version; Therefore, it is not possible to downgrade after upgrading. You can only upgrade to the latest system version.
All of Haier's condensers use copper tubes.
Let me tell you.
That's our game. >>>More