Anonymous users2024-02-11No. 10 steel. It is a kind of steel material, which has good plasticity and toughness, and is easy to be formed by cold and hot processing and normalizing.
Or after cold working, the cutting performance is good, the weldability is excellent, there is no tempering brittleness, hardenability.
and hardenability.
Manufacturing parts that require low stress and high toughness, such as automobile bodies, receptacles, deep-drawn vessels, tubes, gaskets.
It can be used as cold rolling, cold punching, and cold heading.
Formed by cold rolling, hot rolling and other processes, it can also be used as carburizing parts and carbonitriding parts with low core strength.
China GB standard steel grade: 10; China's Taiwan CNS standard steel number S10C; JIS standard steel grade S10C S12C; AISI ASTM standard steel grade 1010 1012;German DIN standard steel grade CK10 C10; BS steel grade 040A10 040A12; French NF standard steel grade XC10 C10; International Standards Organization ISO Standards.
Steel grade C101.
-
Anonymous users2024-02-10The steel plate of steel is a low-carbon steel plate, with a carbon content of about 10% (, and its sulfur (S) and phosphorus (P) impurity element content is generally controlled below (). Tensile strength 410 MPa, yield strength 205MPa, elongation δ5 (%31, section shrinkage 55, hardness: unheattreated, 137HBS, this kind of steel must ensure these requirements at the same time, chemical composition and mechanical properties, we call it usually called excellent carbon steel plate.
10. The plasticity and toughness of the steel plate are very good, easy to be formed by cold and hot processing, good cutting performance after normalizing or cold working, excellent weldability, no tempering brittleness, poor hardenability and hardenability.
-
Anonymous users2024-02-09No. 10 steel plate: 10 is a grade of high-quality carbon structural steel in stamping steel plate. 10 refers to one thousandth of the carbon content.
-
Anonymous users2024-02-08A: No. 10 steel plate (10) is made of high-quality carbon structural steel. The two digits at the beginning of the steel number indicate the carbon content of the steel, expressed in a few parts per 10,000 of the average carbon content.
-
Anonymous users2024-02-07No. 10 steel. It is Chinese GB standard steel number: No. 10.
No. 10 steel has good plasticity and toughness, and is easy to be formed by cold and hot processing, normalizing.
Or after cold working, the cutting performance is good, the welding auspiciousness is excellent, there is no tempering brittleness, and the hardenability and hardenability are poor.
The foreign steel grades corresponding to No. 10 steel are as follows:
1. Japan Shiling JIS standard steel number S10C S12C.
2. American AISI old ASTM standard steel grade 1010 1012.
3. German DIN standard steel number CK10 C10.
4. British BS standard steel grade 040A10 040A12.
5. French NF standard steel grade XC10 C10.
6. ISO standards of the International Organization for Standardization.
Steel grade C101.
-
Anonymous users2024-02-06Summary. Hello! 20 The material of the steel plate is mild steel.
Hello! 20 The material of the steel plate is mild steel.
20 refers to the carbon content of, low-carbon steel is mostly less than; Medium carbon steel is mostly in between; High-carbon steels are mostly greater than. Because of its low strength, low hardness and softness, it is also known as mild steel. It includes most of the ordinary carbon structural steel and some high-quality carbon structural steel, most of which are used for engineering structural parts without hot buried old grinding, and some are carburized and other heat treated for mechanical parts that require pure resistance to bending bucket wear.
Steel plate implementation standard: GB T711 WTB; 20 Steel plate delivery status: hot rolled, normalized, etc. 20 Steel plate characteristics The steel belongs to high-quality low-carbon carbon steel, cold extrusion, carburizing and hardened steel.
The steel has low strength and good toughness, plasticity and weldability. The tensile strength is 253-500MPa and the elongation is 24%. 20 Steel Plate Chemical Composition C:
si ： mn： cr：
Ni: Cu: The mechanical properties of the steel plate refer to the tensile strength of the steel plate
410mpa；Yield strength: 245MPa; Elongation after breakage: 25; Shrinkage rate of broken socks:
55；Do not do impact 20 steel plate use: 20 steel plate is used as a part that does not bear a lot of pressure and requires high toughness, such as tie rods, bushings, screws, lifting hooks, etc., pipes, conduits, carburizing and cyanide parts with little core strength used in large pressure and non-corrosive media below 450, such as bushings, rollers, shafts and gears, sprockets, etc., which are widely used.
-
Anonymous users2024-02-05No. 10 steel isCarbon structural steelthis material.
No. 10 steel belongs to carbon structural steel, referred to as carbon steel, commonly known as excellent steel, No. 10 steel is mainly used to make various parts with high toughness and low load, such as clamps, steel pipes, and gaskets.
Washers, friction plates, automobile bodies, dustproof paints, containers, deep-drawn utensils, enamel products, cold heading bolts and nuts and various welded parts with small load, etc.
Extended information: The corresponding foreign steel grades of No. 10 steel are as follows: 1. Japanese JIS standard steel No. S10C American AISI ASTM standard steel No. 1010 German DIN standard steel No. CK10 British BS standard steel No. 040A10 Li Xiaoa: French NF standard steel No. XC10 International Organization for Standardization ISO standard.
Steel grade C101.
-
Anonymous users2024-02-04No. 10 steel is a class of steel materials.
No. 10 steel has good plasticity and toughness, is easy to be formed by cold and hot processing, has good processing performance, excellent weldability, no tempering brittleness, and requires parts with little stress and high toughness; For example, automobile bodies, receptacles, deep-drawing vehicles, pipes, gaskets, etc., can be used for cold rolling, cold punching, cold heading, cold rolling, hot rolling and other process forming, and can also be used as carburizing parts with low core strength, carbonitriding parts, etc.
However, No. 10 steel also has disadvantages, with poor hardenability and hardenability. China GB standard steel grade: 10; JIS standard steel grade S10C S12C; AISI ASTM standard steel grade 1010 1012;German DIN standard steel grade CK10 C10; BS steel grade 040A10 040A12; French NF standard steel grade XC10 C10; ISO standard steel number C101.
Difference Between No. 10 Steel and No. 20 Steel
1. They are all high-quality carbon structural steels with relatively low carbon content.
2. They are different mainly in two aspects, one is the difference in carbon content; Rather, the mechanical properties are different.
3. From the point of view of chemical composition, the carbon content is different, the average carbon content of 10 steel is 10 parts per 10,000, and the average carbon content of 20 steel is 20 parts of 10,000.
4. Due to the difference in carbon content, their mechanical properties are different.
5. With the increase of carbon content, the strength and hardness of carbon structural steel are increased accordingly, and the plastic toughness is reduced accordingly.
It belongs to low-carbon steel, the strength and hardness are not high, and the plasticity and toughness are very good.
7. Compared with each other, the strength and hardness of 10 steel are lower than those of 20 steel; The plasticity and toughness of 10 steel is better than that of 20 steel.
-
Anonymous users2024-02-03No. 10 steel is a kind of steel material, its plasticity, toughness is very good, easy to cold and hot processing forming, normalized or cold working after cutting, good processing performance, excellent weldability, no tempering brittleness, poor hardenability and hardenability. manufacturing parts that require little stress and high toughness; For example, automobile bodies, receptacles, deep-drawn utensils, pipes, gaskets, etc., can be used as cold rolling, cold punching, cold heading, cold bending, hot rolling and other process forming, and can also be used as carburizing parts with low core strength, carbonitriding parts, etc.
Steel is a material of a certain shape, size, and properties that ingots, billets, or steel are made by pressure processing. Most steel processing is carried out by pressure processing, which causes plastic deformation of the processed steel (billets, ingots, etc.). According to the different processing temperatures of steel, it can be divided into two types: cold working and hot working.
Steel is press-machined into the required material in a variety of shapes, sizes, and properties.
Steel is an indispensable important material for national construction and the realization of the four modernizations, its application is wide, variety, according to the different cross-sectional shapes, steel is generally divided into four categories: banquet profiles, plates, pipes and metal products, and is divided into heavy rail, light rail, large steel, medium steel, small steel, steel cold-formed steel, high-quality steel, wire rod, thick steel plate, thin steel plate, electrical silicon steel sheet, strip steel, seamless steel pipe steel, welded steel pipe, metal products and other varieties.
-
Anonymous users2024-02-02No. 10 steel is a class of steel materials, its plasticity, toughness is very good, easy to cold and hot processing, good cutting performance after normalizing or teasing cooling processing, excellent weldability, no tempering brittleness, poor hardenability and hardenability.
The manufacturing of parts requiring little force and high toughness, such as automobile bodies, receptacles, deep-drawn utensils, pipes, gaskets, etc., can be used for cold rolling, cold punching, cold heading, cold rolling, hot rolling and other process forming, and can also be used as permeable carbon parts, carbonitriding parts with low core strength, etc.
No. 10 mold steel softening
The temperature is 700 720, the holding time is 8 15h, and the cooling speed is 50 100 h, and the temperature is reduced to 550 600 with the furnace, and the furnace is air-cooled.
The hardness was 137HBS before treatment and 118HBS after treatment.
Example of No. 10 die steel application.
1. Cold extrusion die punch, which can be used for cold rolling, cold punching, cold heading, cold bending, hot rolling, hot extrusion, hot heading and other process forming.
2. The manufacturing requirements are not very stressed, and the abrasive parts with high toughness.
The above content refers to Encyclopedia-No. 10 die steel.
Encyclopedia - No. 10 steel.
On the sixth day of October 1972, November 11 in the Gregorian calendar, Scorpio. >>>More
It's made by Libra Generally, people born in October are under this sign People with this sign are very blessed o I am also this sign Hehe.
Summary. Brief Criticism of Personality]: I like a life with order and certainty; Work diligently, easy to achieve ideals; Whenever you encounter unexpected or intractable problems and obstacles, you can be lucky to receive guidance and advice from others; Like hands-on work, interested in pottery, sculpture, fashion design, painting, etc., and can give full play to their talents; When the mood is low, it becomes difficult to communicate, which is easy to cause some confusion. >>>More
The trumpet, also known as the labor trumpet, is a form of song that is closely integrated with the labor process collectively created by laborers in the long-term material production process. In the north of our country, the act of singing trumpets in labor is called "shouting trumpets", while in the south, it is often called "shouting trumpets", "playing trumpets" or "shouting trumpets". In Sichuan and other regions, the "trumpet" is also called "whistle". >>>More
People born on October 5 belong to the zodiac sign: Libra. >>>More