Chemical composition of 1Cr13 stainless steel rods

410 stainless steel rods are martensitic (high-strength chromium steel) stainless steels with good corrosion resistance and machinability. Generally used as steel, cutting tool steel, UNS number is S41000.

Chinese name martensitic stainless steel model American Standard 410; New national standard 12CR13 standard AISI; ASMUNS number S41000.

Chemical Composition: Carbon C:

Manganese mn:

Silicon SI:

Chromium Cr: Nickel Ni:

Phosphorus p: sulfur s:

Note: Unless otherwise indicated, a single value is a high value. When used in some tube making processes, some types of austenitic stainless steels must have a nickel content slightly higher than the values shown in the table; Random; The high ta-content is; High content is; High content is;

410 quenching and tempering process:

580-650 degrees tempered, water-cooled, hardness HBS is 254-302560-620 degrees tempered, water-cooled, hardness HBS is 285-341550-580 degrees tempered, water-cooled, hardness HBS is 254-362520-560 degrees tempered, water-cooled, hardness HBS is 341-388 less than 300 degrees tempered, air-cooled, hardness HBS is greater than 388 Other related issues, please refer to ZBJ36017-1990 industry standard.

Chemical Composition: Carbon C:

Silicon SI:

Manganese mn:

Sulfur s:

Phosphorus p:

Chromium Cr: Nickel Ni: Allowed to contain

What you should express is SUS303Cu, because "303Cu" does not have this grade in the American standard "ASTM A582 A582M", as shown below

SUS303CU belongs to the Japanese standard austenitic stainless steel, and the implementation standard: JIS G4303-2005

The chemical composition of SUS303CU is shown in the following figure:

sus303cu

Japan SUS303CU stainless steel rod can improve machinability, ablation resistance. Suitable for use on automatic lathes. Rivets, screws.

Executive standard: JIS G4303-2005AISI303CU Chemical Composition:

Carbon C: Silicon Si:

Manganese mn:

Phosphorus p: sulfur s:

Chromium Cr:Molybdenum Mo:

Nitrogen n: Copper Cu:

Nickel NI:AISI303CU Mechanical Properties:

Tensile strength: 520

Conditional Yield Strength: 205

Elongation: 40

Section shrinkage: 50

Hardness : 187HB; ≤90hrb;≤300hv

Chemical Composition:

Carbon C:

Silicon SI:

Manganese mn:

Sulfur s:

Phosphorus p:

Chromium Cr: Nickel Ni:

Molybdenum mo: can be joined

Copper cu: Note: Se

Chemical Composition:

c :≤si :≤

mn :≤p :≤

s :≥crni

cumo :≤

Hope it helps.

1. The corresponding grade of 303Cu: German standard: X6Crnicus18-9-2, and the national standard grade: 06Cr18Ni9Cu2 is a kind of stainless steel.

2. Chemical composition of 303cu:

Carbon C: , Silicon Si: , Manganese Mn: , Phosphorus P: , Sulfur S: , Chromium Cr:, Aluminum Al: -

Molybdenum Mo: , Nitrogen N: , Copper Cu:, Nickel Ni:.

3. Mechanical properties of 303Cu: tensile strength: 520, conditional yield strength: 205, elongation: 40, section shrinkage: 50, hardness: 187HB; ≤90hrb;≤300hv

4. 303cu heat treatment specification: solid solution 1010 1150 fast cooling.

303CU Applications:*Suitable for automatic lathes. Rivets, screws.

Mechanical Properties:

Tensile strength b (mpa): quenched tempered, 540 conditional yield strength mpa): quenched tempered, 345 elongation δ5 (% quenched tempered, 25

Section shrinkage quenching and tempering, 55

Impact power AKV (J): quenched and tempered, 78

Hardness: annealed, 200HB; Quenching and tempering, 159HB 1CR13 quenching heating temperature: 1000-1050 degrees, heat preservation for 1 to 3 hours, air cooling, according to the tempering temperature, the hardness is different.

580-650 degree tempering, water-cooled, hardness HBS is 254-302560-620 degrees tempering, water-cooled, hardness HBS is 285-341550-580 degrees tempering, water-cooled, hardness HBS is 254-362520-560 degrees tempering, water-cooled, hardness HBS is 341-388 less than 300 degrees tempering, air cooling, hardness HBS is greater than 388 <>

303cu stainless steel rod, what is its chemical composition?

Hello dear! We'll be happy to answer for you. 303cu stainless steel rod, what is its chemical composition?

Answer: Hello dear dear, SUS303 303CU easy-car stainless steel rod It has good cutting performance, high surface finish and high dimensional accuracy, and is widely used in household appliances and instrumentation industry. Delivery Status:

Flat bars, bars, drawn rods, polished rods, hexagonal steels, forgings and castings and other austenitic stainless steels increase the strength due to their solution strengthening. The chemical composition of austenitic stainless steels is based on chromium and nickel with the addition of elements such as molybdenum, tungsten, niobium and titanium. Because its structure is a face-centered cubic structure, it has high strength and creep strength at high temperatures.

Also due to the large coefficient of linear expansion, the thermal fatigue strength is worse than that of ferritic type stainless steel. 303cu stainless steel rod chemical composition Name: 303cu easy-car stainless steel rod, easy-car stainless steel rod chemical composition (%)c:

si :≤mn :≤p :

s :≥cr ni cu mo :≤

Sulfur : cavity years.

Phosphorium p:

Chromium CR: Bird's Circle.

Nickel ni:

304 stainless steel pipe is a grade of stainless steel produced in accordance with the American ASTM standard.

304 is equivalent to 0cr19ni9 in our country

0Cr18Ni9). 304 contains about 19% chromium and 9% nickel.

Chemical composition (%)

1).c：≤，2).si，3).mn，4).cr，5).ni，6).s，7).p

Excellent resistance to pitting corrosion, high temperatures.

Creep. Excellent strength. 2. Features.

1) The appearance of cold-rolled products is good and beautiful; 2) Due to the addition of MO to Shanghai Shiqiang (SHSQBXG) stainless steel material factory, the corrosion resistance, especially the pitting corrosion resistance, is excellent; 3

Excellent strength at high temperatures; I want stainless steel'

4) Excellent work hardening (weak magnetism after machining) 5) Non-magnetic in the solution state; 6) Compared with 304 stainless steel, ** higher.

3. Scope of application.

For pipelines, heat exchangers, food industry, chemical industry, etc.

304 stainless steel round bar, 304 stainless steel capillary bar.

Grade: 0Cr18Ni9(0Cr19Ni9)C:,Si,Mn,Cr,Ni,S: ,P

Tensile strength (MPa).

min yield strength (mpa).

min elongation (%)

min area reduction (%)

The density of min304 stainless steel.

G cm3 austenitic stainless steel generally uses this value 304 chromium content (%), 304 is equivalent to 0cr19ni9 in China

0Cr18Ni9).

304 stainless steel is a versatile stainless steel material, and the anti-rust performance is stronger than that of 200 series stainless steel materials. The high temperature resistance is also relatively good, which can be as high as 1000-1200 degrees. 304 stainless steel has excellent stainless corrosion resistance and good intergranular corrosion resistance.

For oxidizing acids, it was found in experiments that 304 stainless steel has strong corrosion resistance in nitric acid with a concentration of 65% below the boiling temperature. It also has good corrosion resistance to alkaline solutions and most organic acids and inorganic acids.

Name: 316 stainless steel bar, 304 stainless steel bar, 316 stainless steel bar. Grade: 0Cr17Ni12Mo2, the main material is L S L, 303, etc.

Chemical Composition: Carbon C:

Silicon SI:

Manganese mn:

Sulfur s:

Phosphorus p:

Chromium Cr: Nickel Ni:

Molybdenum mo: