Is the temperature low for ABS pc blue not blue enough?

That's right, blue isn't blue enough, it's probably caused by the low temperature, so you have to fix this low temperature as soon as possible, and then it will suck.

Speaking of which, under normal circumstances, his blue is not blue enough, and he may be caused by the relatively low temperature, and it is also relatively normal.

I just checked for you, and I showed you that if you don't come, the temperature is too low.

In this case, the temperature should be a little lower, and you can turn the temperature up a little bit.

This aspect is completely fine, relatively speaking, it is generally affected by this temperature, so the impact in this regard is relatively large.

It's possible that the temperature is too low for Baohua, and he can still cause such a color, I think the temperature should be relatively low, so he will become such a blue after being inducted.

If ABS and PC blue are not blue enough, it may be caused by too high temperature.

Hello yes, if this happens.

It may be due to the low temperature.

That's right, he should have lowered the temperature a little bit.

Blue is not blue enough, is it low temperature? It's true that the temperature is low, so the blue is not blue enough.

In this case, it is likely to be due to temperature, but it is also possible to be affected by humidity, so it is important to be careful in this regard.

It may be that the temperature is too low, so you can adjust the temperature first to see what kind of state it looks like when the temperature is high.

ABS+PC melting temperature: 230 300C. Mould temperature forming: 50 100C. Injection pressure: Depends on the plastic part PC ABS,

You do say this because we know it's probably because the temperature is relatively low.

ABS plus PC blue is not blue enough, is the temperature low or the temperature is low, and he is fine.

It's still not a case of low temperature, normally speaking, if you can't collect it, the low temperature has a little effect, and if the temperature is normal, it's something else.

If it is blue, the bar must be very low, and generally the higher the position, the redder and the bluer the lower the position.

If the blue is not blue enough, it should not be pure, and it may be adulterated with some other impurities.

Generally, the blue color means that its temperature will be very high, whether it is dark blue or light blue, it already represents its flame height.

If the temperature is low, encouragement is something special that causes you to find a way to raise the temperature for him, right?

Is the temperature low, the boy is not all men, and the temperature must have learned a certain influence.

I am not allowed to use the rules, and I am not allowed to know a follower.

Why isn't blue blue? Does it show the corresponding pair or the lower one?

The molding temperature of ABS+PC material is: 90 120, melting point 160, processing temperature range 180 250, decomposition temperature (in air) 250, general processing temperature is 190 235, mold temperature is generally adjusted at 45 80, and the temperature of fixed mold (front mold) is generally slightly higher than that of moving mold (rear mold) about 5.

PC ABS, polycarbonate and acrylonitrile-butadiene-styrene copolymer and mixture, is a thermoplastic plastic formed by the combination of polycarbonate and acrylonitrile-butadiene-styrene copolymer (ABS), which combines the excellent characteristics of the two materials, the formability of ABS material and the mechanical, impact strength and temperature resistance, ultraviolet (UV) resistance and other properties of PC. Communication equipment, household appliances and lighting equipment.

abs+pc

Melting temperature: 230 300C.

Mould temperature forming: 50 100C.

Injection pressure: Depends on the plastic part.

PC ABS, polycarbonate and acrylonitrile-butadiene-styrene copolymer and mixture, is a thermoplastic plastic made of polycarbonate and polyacrylonitrile (ABS) alloy, combining the excellent characteristics of the two materials, the formability of ABS material and the mechanical properties of PC, impact strength and temperature resistance, ultraviolet (UV) resistance, etc., which can be widely used in automotive interior parts, business machines, communication equipment, home appliances and lighting equipment.

Injection molding process conditions.

Drying treatment: Drying treatment before processing is a must. The humidity should be less than and the recommended drying conditions are 90 110 C, 2 for 4 hours.

Injection speed: as high as possible.

Chemical and physical properties: ABS+PC has the combined characteristics of both PC and ABS. For example, the easy processing characteristics of ABS and the excellent mechanical properties and thermal stability of PC.

The ratio of the two will affect the thermal stability of ABS+PC materials. The ABS+PC hybrid also exhibits excellent flow characteristics. The shrinkage rate is around the right.

Features: ABS+PC is a kind of modified engineering plastic synthesized by mixing. Among them, PC is polycarbonate, and ABS is a copolymer of acrylonitrile (A), butadiene (B) and phenylethylene (S). This modified plastic performs better than PC and ABS alone, for example:

Impact resistance is improved, heat resistance is improved, hardness is improved, and so on.

ABS toughness is better PC ABS is better, but ABS is not resistant to high temperatures and is not fireproof. ABS plastic transmission parts and telecommunication parts. ABS+PC, commonly known as ABS plus polycarbon. The raw material temperature is about 100 and the molding temperature is about 230-250.

There is a certain low temperature resistance, the lowest is about minus 10 degrees, if the weather resistance requirements are high, it is recommended to use super tough and cold-resistant PC, which can withstand cold 40 degrees.

1.Which has better tensile strength and impact resistance between pure PC material and 85%PC + 15% ABS material?

Compared with 85%PC+15%ABS, pure PC material has better impact resistance, tensile strength, brambling strength and hardness, and temperature resistance.

2. According to past experience, in terms of injection molding, PC+ABS is easier to mold than PC and has better fluidity.

3. Appearance color? Pure PC is transparent, colorless and odorless, and it is mostly seen in the market with slightly blue transparent and white transparent. It is generally referred to as white transparent or transparent with a blue background. The PC+ABS alloy is a light ivory-white opaque particle. Generally, plastic parts should need to be colored.

Because the proportion of each grade and alloy combination is different, the above properties will have different changes, and the actual molding shall prevail.

4.The ratio is relatively PC+ABS, with more PC content, good toughness, more ABS content, and good fluidity. Determined by product demand.

PC ABS alloy can combine the excellent properties of both. On the one hand, it improves the heat resistance and tensile strength of ABS, on the other hand, it reduces the viscosity of PC melt, improves the processing performance, and reduces the sensitivity of the internal stress and impact strength of the product to the thickness of the product.

1. Under the conditions of extensive use, it will only show plastic failure, the residual stress is reduced, the stress cracking resistance is improved, and the impact strength is 3 4 times that of PC at room temperature.

2. Excellent boiling water resistance, after 100 and 240 hours of treatment, the tensile strength and bending strength are almost unchanged, and the tensile strength is more than 3 times that of PC treated under the same conditions.

3. Good aging resistance, after hours of treatment, its impact strength is still more than 2 times that of PC.

Fourth, excellent weather resistance, outdoor exposure for 2 years, tensile strength and bending strength are almost unchanged, impact strength is more than 4 times that of PC.

Fifth, the melt viscosity is reduced by 1 3, so the molding temperature can be lower, the molding is easy, the residual stress is reduced, and the color of the product is also better. In addition, the melt viscosity of the blend decreases significantly with the increase of molding pressure, which also improves the formability.

First of all, ABS has better fluidity than PC, so ABS has better fluidity than ABS+PC, so the pressure of injection molding is relatively less than the latter;

Secondly, the injection temperature of ABS is lower than that of PC, so the injection temperature of ABS is lower than that of ABS+PC, so the former is relatively lower than the latter in terms of temperature setting.

The color is affected by many factors, the thickness of the product, the temperature of the forming, and whether the toner is evenly diffused, whether the material is fully baked, and even different machines will cause the difference in color.

PC is generally about 130, PC+ABS 100-110, ABS 90-100;

The above appropriate addition of glass fiber (GF) can increase the heat resistance temperature.

The heat-resistant temperature of a single PC seems to be 120 °, ABS is a little lower than PC, and PC+ABS is not very clear.