The mechanical properties of 1100 aluminum plate, the difference between 1100 aluminum plate and 606

1100 aluminum plate introduction1100 aluminum plate is industrial pure aluminum, aluminum content (mass fraction.

for, it cannot be strengthened by heat treatment. It has high corrosion resistance and electrical conductivity.

and thermal conductivity, its low density, good plasticity, can produce a variety of aluminum through pressure processing, but the strength is low. 1100 aluminum plate.

The processing technology is single, and it is relatively cheap.

Alloy grade 1100 (L6-1) – international standard; Japan: AL100 AL00 (JIS); European Standards:

en aw 1100（en）；France: A45; Canada 990C (CSA); United States: 1100 (AA).

1100 aluminum plate mechanical propertiesTensile strength. b (mpa): 110 136 elongation.

1100 aluminum plate uses1100 aluminum strip is generally used in utensils and heat sinks.

Bottle caps, printed plates, building materials, heat exchanger components, and can also be used as deep-drawn products. It is used in a wide range of fields, from cookware to industrial equipment.

1100 aluminum plate.

The above information is collected and sorted out in the encyclopedia, I hope it will be helpful to you.

Tensile strength b (mpa): 95

Conditional yield strength mpa): 50

Elongation 50mm: 9

1100 aluminum plate and 6061 aluminum plate are different from pro! Hello, glad to answer for you. The differences between Aluminum 1100 and 6061T6 are as follows:

The purity of 1100 aluminum is higher than that of 1100 in terms of strength, density, production cost, and ** are all higher than 1100. Usage: 1100 is generally used as chemical handling and storage equipment, sheet metal products, hollow hardware with drawing cargo spinning, welding combination keys, reflectors, nameplates, etc.

The 6061T6 is used in aviation fixtures, trucks, tower buildings, boats, pipelines and other construction applications that require strength, weldability and corrosion resistance. 1100 is industrial pure aluminum, and the aluminum content (mass fraction) is, which cannot be strengthened by heat treatment. It has high corrosion resistance, electrical conductivity and thermal conductivity, its low density, good plasticity, and can produce various aluminum materials through pressure processing, but the strength is low.

6061-T6 is called aviation duralumin, which is light, high strength, and high production cost, so it is expensive. It has good formability, weldability, machinability, and medium strength, and can maintain good operability after annealing. The range of chemical compositions is the highest content of each other ingredient, the maximum total content of other components, and the balance is al.

Hope mine can help you! Do you have any other questions?

Dear, hello, I am glad to answer for you, what is the hardness of 1050 aluminum plate Answer1050 aluminum plate hardness, because of its different states, the hardness is also different; The hardness value is a range value, not a specific value. 1050 aluminum plate tensile strength b (mpa): 60 100, elongation δ 23, elongation 50mm (%25.

Main characteristics and application scope: industrial pure aluminum has the characteristics of high plasticity, corrosion resistance, good electrical and thermal conductivity, but low strength, not strengthened by heat treatment, poor machinability, and can accept contact welding and gas welding. It is more advantageous to manufacture some structural parts with specific properties of the cluster, such as gaskets and capacitors made of aluminum foil, tube isolation nets, protective sleeves for wires and cables, nets, cores and aircraft ventilation system parts and decorative parts.

Summary. Dear, I am glad to answer for you: the tensile strength of 1050-O aluminum: The tensile strength of 1050A aluminum is between 45-85 MPa, and the maximum alloy tensile strength is about 115MPa.

We are happy to answer for you: the tensile strength of 1050-o aluminum: the tensile strength of 1050A aluminum is between 45-85 megapascals, and the maximum tensile strength of orange lead alloy is about 115MPa.

Aluminum alloy 1050 is pure aluminum, which has high plasticity, high corrosion resistance, electrical conductivity and thermal conductivity, but low strength, heat treatment can not strengthen the machinability is not good; It can be gas welded, hydrogen atom welding and contact welding, and it is not easy to braze; It is easy to withstand all kinds of pressure processing, drawing and bending. Heating 390 430 ; With the effective thickness of the material, the grinding brother is different, and the holding time is 30 120min; Cool with the furnace at a speed of 30 to 50 h to 300 times, and then air cool. 2) Fast annealing:

Heating 350 370 ; With the effective thickness of the material, the holding time is 30 120min; Air or water cooled. 3) Quenching and aging: quenching 500 510, air cooling; Artificial aging 95 105, 3h, air cooling; Natural aging room temperature 120h

Kiss! Hello, glad to answer for you.

The tensile strength of pro-1050-o aluminum is as follows: which degree of tensile strength wheel b (mpa): 60 100 elongation δ (23 elongation 50mm (%251050 aluminum plate hardness, because of its different states, the hardness is also different; The hardness value is a range value, not a specific value.

1050 aluminum plate tensile strength b(mpa): 60 100, elongation δ (23, elongation 50mm (%25. Main features and applications:

Industrial pure aluminum has the characteristics of high plasticity, corrosion resistance, good electrical and thermal conductivity, but low strength, not strengthened by heat treatment, poor machinability, and can accept contact welding and gas welding. Make use of its advantages to manufacture some structural parts with specific properties, such as gaskets and capacitors made of aluminum foil, tube isolation nets, protective sleeves for wires and cables, nets, cores and aircraft ventilation system parts and decorative parts, I hope mine can help you <>

Do you have any other questions? Nothing.

1050 aluminum plate hardness, because of its different states, the hardness is also different; The hardness value is a range value, not a specific value. 1050 aluminum plate tensile strength b (mpa): 60 100, elongation δ (%)

23, elongation 50mm (%)25.

Main features and application scope: industrial pure aluminum has the characteristics of high plasticity, corrosion resistance, good electrical and thermal conductivity, but low strength, not strengthened by heat treatment, poor machinability, and can accept contact welding and gas welding. It makes use of its advantages to manufacture some structural parts with specific properties, such as gaskets and capacitors made of aluminum foil, tube isolation nets, protective sleeves for wires and cables, nets, cores and aircraft ventilation system parts and decorative parts.

Al-al:

Silicon Si : Copper Cu : Magnesium.

Version mg:--zinc zn:

Manganese Mn: Titanium Ti :-Vanadium V: Iron Fe:

Note: Single. Right.

1100 aluminum plate.

It is a pure aluminum plate, and the production process is relatively single, and the first phase is relatively cheap, and the aluminum content is up.

1100 aluminum plate chemical composition zhi

Aluminum AL : Silicon Si : Copper CU : Magnesium MG:--Zinc ZN:

Manganese Mn: Titanium Ti :-Vanadium V: Iron Fe:

Note: Single. 1100 pure aluminum plate.

1100 aluminum plate features1100 aluminum strip belongs to the pure aluminum plate series, its strength is relatively low, and it has excellent ductility, formability, weldability and corrosion resistance; After anodizing, it can further improve the corrosion resistance and obtain an aesthetically pleasing surface; However, it cannot be strengthened by heat treatment.

Calculation method of aluminum content of pure aluminum plateThe pure aluminum plate series determines the minimum aluminum content of this series according to the last two Arabic numerals, for example, the last two Arabic numerals of the 1050 series are 50, and according to the international brand nomenclature principle, the aluminum content must reach the above for qualified products. China's aluminum alloy technical standard (GB T3880-2006) also clearly stipulates that the aluminum content of 1050 reaches the same reason, and the aluminum content of other pure aluminum plate series is also calculated according to this calculation method.