What is zcual10fe3?

CUL10FE3 Organizational Structure.

The metallographic structure of the ingot is a phase + eutectic structure; The cold-pressed structure is a phase and euteclite.

CUL10FE3 has many excellent properties. CUL10FE3 has high strength, hardness and wear resistance, and is commonly used to manufacture gear blanks, threads and other parts. CUL10FE3 has very good corrosion resistance, so it can be used to manufacture corrosion-resistant parts such as propellers.

valves, etc. CUL10FE3 does not spark under impact and can be used to make non-sparking tool materials. It has excellent thermal conductivity.

and stable stiffness, as a mold material in the stretched, rolled stainless steel plate heat exchanger.

It will not produce the advantages of sticking to the mold and scratching the workpiece, and has become a new type of mold material. CUL10FE3 has a shape memory effect and has been used as a shape memory alloy.

to be developed. CUL10FE3 alloy ** is relatively inexpensive and becomes a partial substitute for some Ang*** materials, such as replacing tin bronze.

Stainless steel, nickel-based alloys.

Wait. It is precisely because of the excellent characteristics of CUL10FE3 that it is more and more loved and plays an important role in the civil and military industries.

CUL10FE3 Chemical Composition:

Copper Cu: Margin.

Zinc zn:

Lead PB:

Phosphorus p: aluminium al:

Iron Fe: 2-4

Manganese mn: 1-2

Silicon SI:

Impurities: CUL10FE3 Physical Properties:

Density: Thermal Conductivity:

Cual10Fe3 Chemical Properties:

1. Oxidation resistance: good oxidation resistance at high temperature.

2. Corrosion resistance: It has high corrosion resistance in the atmosphere, fresh water and seawater.

CUL10FE3 Process Performance:

Forming performance: It has good plasticity at high temperature, and can be hot-worked, hot-forging, hot-rolled and hot-forging.

Welding performance: can be good argon arc welding.

Flash soldering can be brazing, but soldering and electroslag welding are not suitable for soldering.

Cutting performance and grinding performance: The cutting performance of the alloy is 30%.

CUL10FE3 is mainly used to make gears, rocker arms, bushings, bearings, disc connectors, bearings, fixing nuts and other high-strength and wear-resistant structural parts, which can be produced in large quantities with stable quality.

ZCUAL10FE3 standard name 10-3 aluminum bronze, commonly known as cast copper alloy, GB 1176-2013, high hardenability, can be used for wear-resistant, mechanical parts such as bushings and inlaid bearings.

ZCUL10FE3 belongs to the national standard cast aluminum bronze, and the implementation standard: GB T 1176-1987

ZCUL10FE3 cast aluminum bronze has high mechanical properties, good wear resistance and corrosion resistance, can be welded, not easy to braze, large castings since 700 air cooling can prevent brittleness.

ZCUL10FE3 cast copper alloy is used for heavy and aggressive castings that require high strength, wear resistance and corrosion resistance, such as shaft sleeves, lead mu nuts, worm gears and pipe fittings working below Huaihail Sen 250.

The chemical composition of Zcual10Fe3 is shown in the following figure:

The physical properties of ZCUAL10FE3 are shown in the following figure:

ZCUL10FE3MN2 belongs to the national standard cast aluminum bronze, and the executive standard: GB T 1176-2013

ZCUAL10FE3Mn2 has high mechanical properties and wear resistance, can be heat treated, has good corrosion resistance and oxidation resistance at high temperatures, has good corrosion resistance in the atmosphere, fresh water and seawater, can be welded, is not easy to braze, and large castings since 700 air cooling can prevent brittleness.

ZCUAL10FE3MN2 is mainly used in parts that require high strength, wear resistance and corrosion resistance, such as gears, bearings, bushings, nozzles, and heat-resistant pipe fittings.

ZCUAL10FE3MN2 Chemical Composition:

ZCUL10FE3Mn2 has high mechanical properties and wear resistance, can be heat treated, has good corrosion resistance and oxidation resistance at high temperatures, good corrosion resistance in the atmosphere, fresh water and seawater, can be welded, not easy to braze, large castings since 700 Song sells fierce air with cold can prevent brittleness.

ZCUL10FE3Mn2 is mainly used in parts that require high strength, wear resistance and corrosion resistance, such as gears, bearings, bushings, nozzle bridges, and heat-resistant pipe fittings.

ZCUAL10FE3MN2 Chemical Composition:

ZCUL10FE3 Cast Aluminum Bronze Material Name: Cast Copper Alloy (10-3 Aluminum Bronze, Metal Type) Grade: ZCUAL10FE3 Standard:

GB T 1176-1987 Features and scope of application: It has high mechanical properties, good wear resistance and corrosion resistance, can be welded, is not easy to braze, and large spring and parallel castings from 700 air cooling can prevent brittleness. Chemical Composition:

Copper Cu: Rest Tin Sn : Impurity Bend Section) Zinc Zn:

Impurities) Lead Pb: Impurities) Nickel Ni: Not included in the sum of impurities) Aluminum Al:

Iron Fe: Manganese Mn: Not included in the sum of impurities) Silicon Si:

Impurities) Note: Sum of impurities Mechanical properties: Tensile strength b (MPa):

Heating Wen buried Sen reputation 1200 1250; Pouring temperature 1100 1180.