Glass shattering effect, the cause of glass breaking

3dmax should work.

No more.

There are two reasons for the general direction of glass breakage:One is that it is damaged by external forces, such as bumps during handling, or human knocks.

The second is that it is not damaged by external forces and naturally ruptures. There are also more impurities, defects, etc., such as bubbles, cracks, impurities, etc., which are present during glass production;

There is also the phenomenon of self-explosion of tempered glass, mainly because of the nickel sulfide in tempered glass. After quenching of tempered glass, the internal nickel sulfide is converted from the high-temperature A phase to the low-temperature B phase, and the volume will increase, which will then lead to the cracking of the glass, which is a normal phenomenon within the specified range.

The balcony is generally made of tempered laminated glass, tempered glass has a certain self-explosion phenomenon, but most of your situation is the action of external force, if it is from the middle point to the surrounding divergence and breakage, it must be damaged by external force.

The deformation of the window causes external stress in a certain direction to the glass, and the stress is concentrated to a certain extent, and the glass is broken.

Is it that the windows are wet and expanding, and the glass is pressed?

It's something that hits it.

After the glass is broken, you need to sweep the glass slag together with a broom, and use wide tape to glue the slag that is not easy to see with the naked eye, wear gloves to prevent hurting your hands, and wrap the glass slag with a transparent bag and put it in a reasonable garbage classification area to prevent injury to the cleaning staff.

After the glass is broken, first use the broom to sweep back and forth several times, the broken glass slag swept together, for those small glass slag that is not easy to find, you can find a wide tape to stick several times in the broken glass place, until the tape can not see the glass slag.

After all the broken glass is collected, wear gloves to prevent your hands from being scratched, then wrap it in a transparent bag, mark the broken glass slag, and put it in a reasonable garbage sorting area to prevent the cleaning staff from indistinguishing and accidentally injuring their hands.

In the future, when there is a similar incident of broken glass, remember how to deal with the broken glass, wear gloves, wear shoes that are carefully punctured, and wrap them in a transparent bag, so as not to hurt your own hands and others at the same time.

There are many reasons for the sudden bursting of glass: 1. It may be damaged by external forces, such as bumps during handling, or artificial knocks. 2. It may also be caused by defects in glass processing factors, such as bubbles, cracks, impurities, etc.

3. Installation factors, if the installation gap is small or the glass is in direct contact with the frame, the edge or corner of the glass will produce extrusion force, inducing glass bursting, etc.

There is also tempered glass.

The self-explosion phenomenon is mainly due to the nickel sulfide in the tempered glass, after the tempered glass is quenched, the internal nickel sulfide is converted from the high-temperature A phase to the low-temperature B phase, and the volume will increase, and then lead to the rupture of the glass, which is a normal phenomenon within the specified range.

Factors that cause the glass to burst and scatter noise.

1. Due to careless handling, installation and maintenance of the glass surface, the edge of the glass is easy to destroy the stress of the glass and cause the self-explosion of the tempered glass.

2. During the installation process, if the installation gap is small or the glass is in direct contact with the frame, the expansion coefficient of the glass and the frame will be irradiated by sunlight.

It is not the same, it is easy to make the edge or corner of the glass produce a squeezing force, inducing glass bursting.

3. Glass processing factors, drilled or cornered glass is easy to burst.

4. Wind disasters such as strong typhoons lead to wind resistance.

Design failure can cause the glass to burst.