What is 16MnCrS5 material?

16MnCr5 is an alloy case-hardened steel that is used, for example, in mechanical engineering components. The steel can be m-treated to optimize its machinability.

16MnCr5 steel contains smooth, deformable calcium aluminate, encapsulated in manganese sulfide as an alternative to tough alumina inclusions. Calcium-treated metal is used for inclusion correction.

Here are a few diagrams to briefly illustrate:

16mncr5 chemical composition.

16MnCr5 mechanical properties.

16mncrs5 alloy steel16mncrs5 material number:16mnCRS5 standard:en 10084 :

16mncrs5 characteristics and applications:16mncrs5 material, German grade special steel.

16mncrs5 chemical composition:Carbon C: -

Silicon SI:

Manganese mn: 1 -

Phosphorus p: sulfur s: -

Chromium cr: -

16mncrs5 main specifications:16mncrs5 round bar, 16mncrs5 forging bar, 16mncrs5 plate, 16mncrs5 flat bar, 16mncrs5 forging, 16mncrs5 forging ring, 16mncrs5 machining piece, 16mncrs5 pipe, 16mncrs5 forging cake.

16mncrs5 is alloy steel, 16mncrs5 (alloy structural steel, material number:

Grade: 16mncrs5

Standard: EN 10084: 2008

Features & Applications:

16mncrs5 material, German grade special steel.

Chemical Composition: Carbon C: -

Silicon SI:

Manganese mn: 1 -

Phosphorus p: sulfur s: -

Chromium cr: -

16mncrs5 is a German case-hardened non-alloy structural steel. Chemical composition: , si , p , s ,

16mncrs5(EN steel is an alloy steel that is used for initial forming into a forged product. is the EN numeric mark for this material. 16MnCRS5 is the EN chemical name. In EN forged alloy steel, it has a lower embodied energy and a lower base cost.

Alloy structural steel has sufficient plasticity and toughness, with high yield strength, tensile strength, endurance strength, yield ratio (generally about.

This steel has a high content of alloying elements, mainly corrosion-resistant steel, heat-resistant steel, wear-resistant steel and other special steels with physical and chemical properties. Alloy structural steel has better mechanical properties than carbon structural steel, especially high heat treatment performance.

16mnCrS5 (EN chemical composition.

c（％）si（％）

mn（％）p（％）

s（％）cr（％）

mo( nickel ( ).

16mncrs5(en mechanical properties - heat working, heat treatment and hardness.

Hot working temperature: 1150 850

Heat treatment temperature |Annealing: 650 700

Heat treatment temperature |Carburizing: 880 980

Heat treatment temperature |Quenching (center): 860 900

Heat treatment temperature |Quenching (surface): 810 840 oil.

Heat treatment temperature |Tempering: 170 210

Hardness HBS after annealing: 207

16mncrs5 (EN Typical Applications.

Alloy structural steel is widely used in ships, vehicles, aircraft, guided missiles, railways, bridges, pressure vessels, machine tools, mechanical parts with large cross-sectional dimensions and other fields.

The material is characterized by processing and carburizing, depending on where you're using it.

16mncrs5 belongs to the European standard "guaranteed hardenability carburizing steel", the implementation standard: EN 10084-2008

16MnCRS5 is a steel grade imported from Germany, which is equivalent to 16CrMnh steel in China (refer to GB T 5216-2004), which has good hardenability and machinability, and can obtain higher surface hardness and wear resistance after heat treatment for larger cross-sectional parts, and high impact toughness at low temperature. 16mncrs5 gear steel is used after carburizing and quenching, and is mainly used to manufacture gears, worms, sealed shaft sleeves and other parts.

The chemical composition of 16MnCrS5 is shown in the following figure:

16mncrs5 is an alloy case-hardened steel that is used, for example, in mechanical engineering components. The steel can be m-treated to optimize its machinability. Specifically, ** is one ton of yuan.

16Mncrs5 steel contains smooth, deformable calcium aluminate, encapsulated in manganese sulfide as tough alumina.

Substitute for inclusions. Calcium cavity roll-treated metal is used for inclusion correction.

16MnCRS5 is a steel grade imported from Germany, which is equivalent to 16CrMN H steel in China (refer to GB T 5216-2004) and has good hardenability.

and machinability, for larger cross-sectional parts, after heat treatment, higher surface hardness and wear resistance can be obtained, and the low-temperature impact toughness is also higher. 16mncrs5 gear steel is used after carburizing and quenching, mainly used to manufacture gears and worms.

Sealed bushings and other parts.

16mncrs5 material number:

16mnCRS5 standard:

en 10084 : 2008

16mncrs5 characteristics and applications:

16mncrs5 material, German grade special steel. It is equivalent to China's 16CRMNH steel (refer to GB T 5216-2004), which has good hardenability and machinability, and can obtain higher surface hardness and wear resistance after heat treatment for larger cross-section parts, and the impact toughness of low Wang blocking temperature is also higher.

16mncrs5 gear steel is used after carburizing and quenching, and is mainly used to manufacture gears, worms, dense fiber tung seal shaft sleeves and other parts.

16mncrs5 chemical composition:

Carbon C: -

Silicon SI:

Manganese mn: 1 -

Phosphorus p: sulfur s: -

Chromium cr: -

16mncr5 carburized steel16MnCR5 Introduction:16MnCr5 is a steel grade introduced from Germany, which is equivalent to 16CrMnH steel in China (refer to GB T 5216-2004), which has good hardenability and machinability, and can obtain higher surface hardness and wear resistance after heat treatment for larger cross-sectional parts, and high impact toughness at low temperature. 16Mncr5 gear steel is used after carburizing and quenching, and is mainly used to manufacture gears, worms, sealed shaft sleeves and other parts.

16mncr5 standard:gb/t 3077-1988

jis g4053:2003

a29m:2005

iso 683-18:1996

en 10084-2008

16mncr5 corresponding grade:16mncr5 chemical composition. Carbon C: -

Silicon SI:

Manganese mn:sulfur s:

Phosphorus p:

Chromium cr: -16MnCr5 mechanical properties:Tensile Strength B (MPa): 1373

Conditional yield strength (mpa): 1187

Elongation δ5 (%13

Section shrinkage (57

Impact toughness value ku (j cm2): 72

16mncr5 Delivery Status:Annealed delivery.

There is a lot of market for this material. The unit price will not be high.

16mncr5 belongs to the European standard "guaranteed hardenability carburizing steel", the implementation standard: EN 10084-2008

The chemical composition of 16MnCr5 is shown in the following figure:

From the perspective of chemical composition, 16MnCr5 is equivalent to the domestic grade "16CrMnH".

About 13,000 tons of resin sand production.