16mncr5 belongs to the European standard "guaranteed hardenability carburizing steel", the implementation standard: EN 10084-2008
16MnCr5 is a steel grade introduced from Germany, which is equivalent to 16CrMnH steel in China (refer to GB T 5216-2004), which has good hardenability and machinability, and can obtain higher surface hardness and wear resistance after heat treatment for larger cross-sectional parts, and high impact toughness at low temperature. 16Mncr5 gear steel is used after carburizing and quenching, and is mainly used to manufacture gears, worms, sealed shaft sleeves and other parts.
The chemical composition of 16MnCr5 is shown in the following figure:
-
German standard alloy special steel.
EN steel is a type of alloy steel that is used for primary forming into a forged product. is the EN numeric mark for this material. 16MnCr5 is the EN chemical name.
In EN forged alloy steel, it has a lower embodied energy and a lower base cost. EN steel (16MnCr5 material) is a European standard carburizing steel (case-hardened steel) with good hardenability and machinability. For parts with larger cross-sections, heat treatment results in high surface hardness and wear resistance, as well as high low-temperature impact toughness.
en Execution Standards.
EN 10084:2008 Case-hardened steel. Technical terms of delivery.
EN 10132-2:2000 Cold-rolled narrow strip for heat treatment. Technical delivery conditions. Carburized steel.
EN 10263-3:2001 Steel rods, steel rods and wires for cold and cold extrusion. Technical delivery conditions for case-hardened steels.
EN 10297-1:2003, Seamless round steel pipes for mechanical and general engineering purposes. Non-alloy and alloy steel pipes.
German standard material number: German standard steel number: 16mncr5
Chemical composition: c: 0,14 - 0,19
si:max. 0,40
mn:1,00 - 1,30
p:max. 0,035
s:max. 0,035
cr:0,80 - 1,10
EN steel's properties include four common variations.
FP annealed (+FP) steels Hardened (+H) steels.
Spheroidized (+AC) Steel Spheroidized and cold-drawn (+AC+C) steel.
Mechanical properties of steel (16mncr5 material).
Material, 16mncr5 steel Brinell hardness.
Soft annealing: 207 hbw
Hardness treated: 156-207 HBW
Treated ferrite-pearlite structure and hardness: 140-187 HBW
Standardization: 138-187 HBW
EN, 16MnCr5 tensile strength (after quenching and tempering at 200 °C).
-
It is equivalent to 15crmn of the national standard, which is malleable.
-
16mncr5 belongs to a grade of German standard, in the national standard of the material corresponding to 15crmn, it does not seem to be 20crmo, in the market is now this material is relatively small, but Xingcheng, Guigang, Fushun and other steel mills also still have the production of 16mncr5 this material.
-
16MnCR5 implementation standard EN 10084-1998, is a steel grade imported from Germany, equivalent to China's 16CRMNH steel (refer to GB T 5216-2004), with good hardenability and machinability, for larger cross-section parts, heat treatment can obtain higher surface hardness and wear resistance, low temperature impact toughness is also higher.
Chemical Composition: Carbon C:
Silicon SI:
Manganese mn:sulfur s:
Phosphorus p:
Chromium Cr: Uses: 16mncr5 gear steel is used after carburizing and quenching, mainly used in the manufacture of gears, worms, sealing sleeves and other parts.
-
16MnCr5 steel plate is German standard alloy structural steel, 16Mncr5 (structural steel carburized steel.
Executive standard: EN 10084-1998
Characteristics and scope of use:
It is a steel grade introduced from Germany, which is equivalent to 15crmn steel in China, which has good hardenability and machinability, and can obtain higher surface hardness and wear resistance after heat treatment for larger cross-section parts, and high low-temperature impact toughness. After carburizing and quenching, it is mainly used to manufacture gears, worm gears, sealed shaft sleeves and other parts.
Chemical Composition: Carbon C:
Silicon SI:
Manganese mn:sulfur s:
Phosphorus p:
Chromium Cr: Specification for heat treatment and metallographic structure:
Heat treatment specification: 900 oil quenching + 870 oil quenching, 200 tempering.
Metallographic structure: tempered martensite.
16MnCr5 mechanical properties:
Tensile Strength B (MPa): 1373
Conditional yield strength (mpa): 1187
Elongation δ5 (13
Section shrinkage (57
Impact toughness value ku (j cm2): 72
Hardness: 297HB,
-
16mncr5 alloy structural steel.
Material Name: Guaranteed Hardenability Structural Steel.
Standard: GB T 5216-2004
Chemical Composition: Carbon C:
Silicon si:manganese mn:
Sulfur s: Promised residual content
Phosphorus p: Promised residual content
Chromium Cr: Nickel Ni: Promised Residual Content
Copper cu: Promised residual content
Mechanical properties. Hardness: annealed or tempered at high temperature, 197HB, indentation diameter Delivered in rolled or forged condition. According to the requirements of the buyer, it can also be delivered in the condition of heat treatment (normalizing, annealing or high temperature tempering). The delivery status should be indicated in the contract.
-
16mncr5 belongs to the European standard "guaranteed hardenability carburizing steel", the implementation standard: EN 10084-2008
The chemical composition of 16MnCr5 is shown in the following figure:
From the perspective of chemical composition and performance, 16MnCr5 corresponds to the domestic grade "16CrMnH".
-
Yes, not much of a problem.
-
Tensile Strength B (MPa): 880-1180 Conditional Yield Strength MPa): 635
Elongation δ5 (%9
Section shrinkage (57
Impact toughness value ku (j cm2): 34
Hardness: 297HB,
Specimen size: a sample.
16mncr5 heat treatment specification and metallographic structure:
Heat treatment specification: 900 oil quenching + 870 oil quenching, 200 tempering.
Metallographic structure: tempered martensite.
Uses: Manufacture gears, worms, plastic molds, turbine oil seals and gasoline sleeves, etc.
-
16mncr5 belongs to the European standard "guaranteed hardenability carburizing steel", the implementation standard: EN 10084-2008
The chemical composition of 16MnCr5 is shown in the following figure:
16mncr5 alloy steel, the number indicates the element content >>>More
It's easy to die there, level 38 is a bit low, you can't pass normal, and it's easy to wait for 45.
You can search for "Zhou Yi Fortune Measurement" on it, which is written in detail.
The year 1986 is the year of the Gregorian calendar, and the Gregorian calendar uses a numerical year. The lunar calendar is chronological. >>>More
On the 10th day of the fourth month of the year.
Eight characters: Ding Chou Yi Si. >>>More