Liquid cement based permeable crystalline waterproof material does not smash the floor tiles, is it

1.There is no liquid cementitious permeable crystalline waterproofing material.

2.If you want to use cement-based permeable crystalline waterproof materials to repair, it should be treated from the back water surface, there are prerequisites, it can not be a water pipe leakage, and the waterproof around the bathroom should be good enough, but a small amount of water used leaks under the tiles and then leaks to the bottom, otherwise it may be more and more miserable!

With many years of experience in the home improvement waterproofing industry, this can only appear in theory, and it is impossible in practice.

Cementitious permeable crystalline waterproofing materials are in liquid form. However, this type of material does not penetrate well into the tile. It can only penetrate through the gaps between the tiles (the gaps in the tiles are very small or even none.

Very few can penetrate it. It can only form a thin film layer on the surface of the tile, and the tile has a glazed layer on the surface that is smooth, and the film layer formed is difficult to bond firmly with the tile; And the waterproof coating is not resistant to abrasion and external damage. In summary:

It is ineffective to repair the bathroom with cement-based permeable crystalline waterproof material without smashing the floor tiles. It's just the hype of some merchants to deceive users.

There are no cement-based permeable crystalline waterproofing materials are liquid, and there are two standard materials for cement-based permeable crystalline waterproof materials, one is cement-based permeable crystalline waterproof coating for powder brushing, and the other is cement-based permeable crystalline waterproofing agent, which is also used as powder for adding to concrete. The permeable crystallization of the liquid is fooling!

Summary. Dear, I am glad to answer for you: cement-based permeable crystalline waterproof coating can be used externally to block internal water, which can be used for various cast-in-place or precast concrete, reinforced concrete and prestressed reinforced concrete, and concrete structures and high-performance concrete that require good waterproofness, frost resistance, corrosion resistance and other durability indicators.

Such as tunnels, subway systems, bridges, dams, culverts, basements, canals, industrial and civil construction engineering concrete, etc.

Dear, I am glad to answer for you: cement-based permeable crystalline waterproof coating can be used externally to block internal water can be used for a variety of cast-in-place or precast concrete, reinforced concrete and prestressed reinforced concrete and concrete structures and high-performance concrete that require good and spring waterproofing, frost resistance, corrosion resistance and other durability indicators. Such as tunnels, subway systems, bridges, dams, culverts, basements, canals, industrial and civil construction projects mixed with concrete-resistant soil, etc.

Check and confirm that the pipe joints and test section are tightly and firmly sealed. The nozzles and branch ports at both ends of the test section are sealed and plugged, and 24 walls are sealed with 1:3 cement mortar bricks, and the surface is sealed, and the test can be carried out only after curing to a certain strength of the sliding cover.

Hello, I am glad to answer for you that cement-based permeable crystalline waterproof coating is non-toxic and environmentally friendly, and the following are its advantages: 1. It has double waterproof performance: the permeable crystals it produces can penetrate deep into the concrete structure to block the structural pores, no matter how much its penetration depth is, it can be used by Fanchang to play a role in the structure to congratulate the waterproofing, and at the same time, the coating acting on the base surface of the concrete structure can play a role in compensating for shrinkage due to its micro-expansion performance, so that the structural base surface after construction also has a good anti-cracking and impermeability effect.

Xun file 2, has a very strong water pressure resistance: it can withstand strong water pressure for a long time, in the thickness of 50mm, the compressive strength of the concrete specimen painted on two layers of the material, at least can withstand the water pressure (. 3. It has a unique self-healing ability

This product is an inorganic waterproof material, the crystals formed will not produce aging, the crystal structure can still activate the cement and produce new crystals after many years of water, and the crystals will continue to compact, seal or reseal the cracks or pores smaller than the one, and complete the process of self-repair.

Cement-based permeable crystalline void waterproof coating can be used for household waterproofing, it is a high-efficiency water-based waterproof material in Liling, which can be quickly and deeply absorbed by cement and mud sand materials. The material has excellent impermeability and can effectively prevent moisture and moisture from causing damage to the buildingAt the same time, it has good acid and alkali resistance, which can effectively remove the moisture that has not yet solidified and prevent the wall from cracking. In addition, the material also has a certain water storage function, which can resist drought.

Kiss Glad to answer for you, my answer is as follows: Kiss, cement-based permeable crystallization waterproofing agent can be used for benzene board penetration. Expand the use and construction method of cement-based permeable crystalline waterproof coating Main uses of cement-based permeable crystalline waterproof coating masterbatch:

Cement-based permeable crystalline waterproof coating is mainly used in the waterproof construction of the surface of the concrete structure, the leakage plugging construction of structural cracking and seepage point holes, the waterproof and plugging construction of reservoirs, cooling towers, dams, tunnels, roof squares, parking platforms, elevator pits, swimming pools, food storage, sewage pools, bridge structures, aquariums, granaries, highways, airports, aprons, oil pools, sports fields, subway stations, underground diaphragm walls, tunnels, culverts, reservoir dams, industrial and civil basements, roofs, toilets, Waterproofing of all cement-based surfaces of bathhouse concrete building facilities, as well as maintenance of all cement structural defects of concrete construction facilities.

Summary. Hello dear, permeable crystallization and cement mixing can really be waterproof and leak-proof. Permeable crystalline waterproof coating is an active substance with a molecular structure of active silicon, with a small molecular weight, and contains both hydrophobic and hydrophilic groups, which are more hydrophilic than hydrophobic, soluble in water, and do not occur polycondensation crystallization in dry environments, but polycondensation crystallization occurs in humid environments.

It is a mixture of active silicon, cement, active inorganic mixture, etc.

Hello dear, permeable crystallization and cement mixing can really be waterproof and leak-proof. Permeable crystalline waterproof coating is an active substance with a molecular structure of active silicon, small molecular weight, and contains hydrophobic groups and hydrophilic groups, which are more hydrophilic than hydrophobic, soluble in water, and do not occur polycondensation crystallization in a dry environment, but polycondensation crystallization occurs in a humid ridge loss environment. It is a mixture of active silicon, cement, active inorganic mixture, etc.

The active masterbatch is dissolved in water during the cement hydration process or during the construction on the wet surface of the cement products, and is dispersed in the cement products with water, but with the growth of time, the water is mixed with the hydration reaction of the cement, and a part of the water is volatilized and lost, resulting in the increase of the concentration of the active aqueous solution and the occurrence of polycondensation crystallization.