The painting steps of blue and white porcelain, how to make blue and white porcelain

Tools Raw materials: colored pencils, notebooks, pencils, erasers.

Method Steps:

1. First of all, we painted blue and white porcelain.

The mouth of the bottle is an oval shape. Then draw the body of the bottle, and the sides should be symmetrical.

2. Then draw the bottom of the bottle and carefully observe the shape of the bottom of the bottle. Decorate the neck with wavy threads, which should be rounded.

3. Then draw an arched decorative pattern at the top of the bottom of the bottle. Two arches were also painted on both sides.

4. Then draw two wavy lines above the arch.

5. Draw a flower in the center of the blue and white porcelain, and the petals are heart-shaped.

6. Draw another small flower next to it in the same way. Then draw some s-shaped patterns around the flowers to give them a touch of touch.

7. Finally, we paint the painted blue and white porcelain with beautiful colors.

Tools Ingredients: color brushes, drawing books, pencils, erasers.

Method Steps:

1. First of all, we first draw the mouth of the blue and white porcelain, which is an oval. Then sketch out the body of the bottle, and draw the sides symmetrically.

2. Then draw the bottom of the bottle and carefully observe the shape of the bottom of the bottle. Decorate the bottleneck with wavy lines, and draw rounded lines.

3. Then draw a pattern on the top of the bottom of the bottle, the shape of an arch. Two more arches are drawn on each side.

4. Then draw two wavy lines above the arch.

5. Draw a flower on the ** of blue and white porcelain, and its petals are heart-shaped.

6. Draw a small flower next to it in the same way. Then draw some S-shaped patterns around the flower to embellish it.

7. Finally, we can paint the painted blue and white porcelain with a beautiful color.

First, knead the mud. The purpose is to empty the air bubbles in the mud and make the mud more compact.

Second, make blanks. The blank is made according to the final design of the instrument type to make the roughly corresponding blank body, for the later printing of the blank for use, the traditional process is mostly completed by manual drawing.

Third, the blank. The rough billet is made and dried in the natural shade after a certain period of time.

Fourth, glaze. For porcelain production, if there is no decoration in the vessel, it needs to be glazed first.

Fifth, draw blanks. If the blank with a good inner glaze is applied, you can enter the blank painting process.

Sixth, mixed water.

Seventh, the glaze. The porcelain embryo that has been painted and decorated is covered with a layer of glaze, and there are generally methods such as sticking glaze, brushing glaze, dipping glaze, and blowing glaze.

Eighth, firing kilns. The porcelain blanks to be fired are evenly distributed in the kiln body, which is called a full kiln.

Blue and white porcelain, also known as blue and white porcelain on white ground, often referred to as blue and white, is one of the mainstream varieties of Chinese porcelain, belonging to underglaze colored porcelain. Blue and white porcelain is made of cobalt ore containing cobalt oxide as raw material, depicting ornamentation on the ceramic body, and then covering with a layer of transparent glaze, which is fired at one time by a high-temperature reduction flame. The cobalt material is blue after firing, and has the characteristics of strong tinting strength, bright color, high firing rate and stable color.

Blue and white porcelain pattern painting steps:

1. Draw an oval shape first as the mouth of the blue and white porcelain.

2. Then outline its bottle body, and the symmetry to be drawn on both sides.

3. Draw the bottom of the bottle and decorate the bottleneck with wavy lines.

4. Draw an arch-shaped pattern on the top of the bottom of the bottle.

5. Draw a wavy line pattern in the middle of the bottle body, and draw two flowers and an S-shaped pattern.

6. Paint the color, so that the blue and white porcelain is painted.

Features of blue and white porcelain:

Blue and white is the use of natural cobalt material on the white clay for painting decoration, and then covered with transparent glaze, and then fired at a high temperature of 1300 degrees Celsius, so that the pigment fully penetrates into the glaze, showing a verdant blue pattern, which looks beautiful and beautiful, clear and elegant. Blue and white porcelain decoration is the most national decoration in China, a kind of underglaze colored porcelain, and one of the earlier methods of ceramic decoration in China.

1. The first step is the conventional composition positioning, in this step, the painter should arrange the blue and white porcelain vase reasonably in the picture.

2. The second step is to draw the large external shape and main structure of the blue and white porcelain vase, in this step, the painter should use lighter lines to draw the shape and main structure of the blue and white porcelain vase.

3. The third step of the expression step of the blue and white porcelain vase is to lay a large light and dark tone, in this step, the painter should evenly coat the backlit part of the blue and white porcelain vase with a pencil color.

4. The fourth step of the performance step is in-depth depiction, which is to carefully express the subtle changes of the bright and gray sides of the blue and white porcelain vase and the reflection of the dark side.

5. The last step of the steps is to adjust and finish the picture.

What are you going to draw? Oil painting or gouache or what?

If you know how to draw and have a foundation, then it's good to draw.

The production process of blue and white porcelain is as follows:

1. Knead the mud. The purpose of mud kneading is to empty the air bubbles in the mud, so as to further tighten the mud. If this process is missing, it will be easy to have bubbles in the body, and if the body is too dry, it is easy to break and deform when the hole is burned.

2. Make blanks. Jingdezhen traditional round ware blank making, that is, according to the final type of the body to make roughly the corresponding body, for the later production of blanks.

3. Printing blank. The finished rough blank can enter the printing process after a certain period of natural drying. The purpose of the blank is to make the hand-formed round ware achieve uniformity after firing.

After the hand-drawn body Sun Shengzhong naturally dries, the semi-dry body is placed on the earthen grinding tool and patted by hand, so that the body is evenly formed around it.

4. Billet. The billet is to finish the printed billet to make it further smooth and round.

5. Dangli glaze.

For round ware production, if there is no decoration in the vessel, it needs to be glazed first. The glaze on the outside of the ware is the second dipping glaze in the later period. Glaze is a thin layer of glass attached to the surface of the ceramic body, which has similar physical and chemical properties to glass.

The glaze is generally made of quartz, feldspar, clay and other mountains.

6. Draw blanks. After swinging the inner glaze, you can enter the blank painting process. The blue and white material used in the painting blank needs to be ground and formulated for a long time in advance, which is inseparable from each studio.

7. Apply outer glaze.

After the painting is completed, a second glazing process is required. At this time, the bottom foot of the cup has not yet been formed. The dipping method requires the master to have a comprehensive understanding and grasp of the body, glaze and what to expect from the porcelain.

The length of time the porcelain blank is immersed in glaze water directly affects the quality of the porcelain after firing.

8. Full kiln and firing kiln.

The porcelain blanks to be fired are evenly distributed in the kiln body, which is called a full kiln. When the kiln is full, it is necessary to place it reasonably according to the structure size of the kiln body and the size of all the green bodies to be burned, and leave a reasonable fire flue, otherwise it will affect the atmosphere in the kiln body during firing, resulting in firing failure.

9. Open the kiln. After 12-18 hours of natural cooling, when the temperature in the kiln body drops to normal temperature, the kiln can be opened. This is the most exciting part of the entire production process.

The steps to draw a simple and beautiful blue and white porcelain are as follows:

Prepare materials: 1 piece of A4 paper, 1 pencil, 1 set of watercolor pens.

1. First draw the mouth of the blue and white porcelain. The mouth of the blue and white porcelain bottle is generally an oval shape. Then draw the body of the vase, and the body of the bottle should be symmetrical.

2. Then draw the bottom of the vase, and you can draw some lines on the neck of the bottle to decorate it.

3. Then draw some patterns on the top of the bottom of the bottle to decorate the bottom of the bottle.

4. Continue to do some patterns to decorate the mold.

5. We can use our imagination to paint patterns on the body of the blue and white porcelain bottle.

6. Finally, we paint the blue and white porcelain, and it's okay.

Blue and white porcelain: blue and white porcelain, also known as blue and white porcelain on white ground, blue and white, is a kind of high-temperature underglaze porcelain with blue flowers on white ground and blue flowers originating from China and all over the world, which is a treasure of Chinese ceramic firing technology and one of the mainstream varieties of Chinese land wheel porcelain.

Blue and white porcelain was produced in the Tang Dynasty, flourished in Jingdezhen in the Yuan Dynasty, and reached its peak in the Kangxi period of the Qing Dynasty. It uses cobalt ore containing cobalt oxide as raw material, depicts the decoration on the ceramic body, and then covers it with a layer of transparent glaze, which is fired at one time by a high-temperature reduction flame, and has the characteristics of strong tinting strength, bright color, high firing rate and stable color.

Blue and white porcelain types:

The ancient blue and white porcelain of the author's country, the painting decoration is delicate and elegant, the text at the bottom of the porcelain, the pattern is varied, and the style of each period has distinctive characteristics of the times. According to the form and type of blue and white porcelain, it can be mainly divided into five categories: chronicle model, auspicious words, hall name, praise model and ornamental model.