What are the characteristics of the turquoise green glaze used in the green bottom of Qianlong porce

The turquoise green glaze used in the green bottom of the porcelain in the Qianlong period has the following characteristics:

1.The color of turquoise green glaze is pale yellow with a slight greenishness, which is similar to the color of turquoise, so it is named "turquoise green". This glaze is often used as a color ground for colored porcelain to highlight the beauty of the painting.

2.Turquoise green glaze is a low-temperature colored glaze, and its firing temperature is low. Because blending requires a certain amount of skill and experience, it can be evenly and thickly moistened after firing.

3.When the Qianlong Dynasty's "green and green" porcelain is viewed from the side of the light, the glaze will have very fine wrinkles, like a fine wave formed by a breeze blowing through a calm lake.

In general, the turquoise green glaze used in the green bottom of the porcelain in the Qianlong period is a low-temperature color glaze with a unique color, a certain skill required for blending, and a uniform and thick after firing.

Turquoise green glaze resembles turquoise because of the glaze color.

And the name, is a new variety of Qing Dynasty monochrome glazed porcelain, its color is light yellow in the slight green, similar to the color of turquoise, so the name "turquoise green". Turquoise green glaze is often mostly colored porcelain to highlight the beauty of painting, and this type of process is not only so, but also highlights the uniform texture of turquoise green glaze. Although the turquoise green glaze is a low-temperature color glaze, the deployment is also quite laborious, and the uniform effect can be obtained when the color is applied properly, and the feeling of uniform and thick moisture is now uniform after firing.

The Qianlong Dynasty's "green mile and green bottom" has very fine wrinkles on the glaze surface, like a fine wave formed by a breeze blowing through a calm lake.

The main ingredients of the porcelain turquoise green glaze formula in the Qianlong period include <> these: 1Porcelain clay:

Kaolin, quartz and feldspar are the main components used to provide the base material for porcelain. 2.Stone material:

Including quartz, feldspar, pyroxene and other burning granular ores, used to increase the texture and effect of the glaze. 3.Green Pigments:

Common green pigments include chromium-containing alum and chromium-containing chromium oxide, which can give the glaze of the porcelain section a bright green color. 4.Alkaline & Flux:

Alkali metal oxides such as sodium carbonic acid, potash carbonic acid, etc., are used to reduce the melting point and increase the fluidity and transparency of the glaze. 5.Stabilizer:

Such as silicic acid, potassium hydrohydroxy phosphoric acid, etc., are used to increase the stability of the glaze and prevent cracking. 6.Pigments and colorants:

Such as metal oxides and metal particles (such as copper, manganese, iron, etc.), which are used to adjust the depth of the glaze color and add texture effect. It should be noted that the specific formula may vary depending on the era, region and kiln mouth, and this is just a general <>ingredient reference

Summary. What are the ingredients in the formula of porcelain turquoise green glaze during the Qianlong period, as follows: The formula ingredients of porcelain turquoise green glaze are made of a mixture of pigments such as copper oxide, iron oxide, chromium oxide and cobalt oxide.

Among them, copper oxide is the main component, which produces a green color, while iron oxide and chromium oxide can adjust the depth and brightness of the color, and cobalt oxide can increase the gloss of the glaze. In addition, it is also necessary to mix appropriate raw materials such as quartz, feldspar, and china clay, as well as add the appropriate amount of flux and control agent to ensure that the glaze is melted and evenly coated on the surface of the porcelain.

What are the ingredients in the formula of porcelain turquoise green glaze during the Qianlong period, as follows: The formula ingredients of porcelain turquoise green glaze are made of a mixture of pigments such as copper oxide, iron oxide, chromium oxide and cobalt oxide. Among them, copper oxide is the main component, which can produce the color of late vertical green wax, while iron oxide and chromium oxide can adjust the depth and brightness of the color, and cobalt oxide can increase the gloss of the glaze.

In addition, it is also necessary to mix appropriate raw materials such as quartz, feldspar, and china clay, as well as add the appropriate amount of flux and control agent to ensure that the glaze is melted and evenly coated on the surface of the porcelain.

Porcelain turquoise green glaze was a very popular glaze color in the Qianlong period, and it was often used to make court porcelain and export porcelain. This glaze is characterized by the freshness and brightness of the color rock, high gloss, and different hues under different lights, giving people a sense of smoothness and change. In the production process, it is necessary to master the composition and ratio of the glaze, as well as the temperature and time of firing, in order to be able to produce high-quality turquoise green glazed porcelain.

Summary. 1.Turquoise green glazed porcelain, showing blue-green, not pure green as we understand it today, a little yellowish, yellow with green; 2.

Qing Dynasty turquoise green glazed porcelain was created in Yongzheng, Yongzheng did not have turquoise glazed porcelain before, if someone takes a Ming Dynasty turquoise green glazed porcelain, it is definitely not right, so this provides a theoretical basis for your appreciation; 3.The turquoise glazed porcelain of Yongzheng and Qianlong is delicate, the glaze color is uniform, and there is a sense of uniformity and heaviness; 4.Qianlong turquoise green glaze ware is mostly small pieces of cultural toys and ornaments, and large pieces are rare, not that there are none; 5.

The turquoise glaze after Jiaqing is dark green, while the Yongzheng and Qianlong periods are lighter.

Hello, it is a pleasure to serve you, and the question you asked is: Who made the turquoise green glazed porcelain of Qianlu Xulong The answer is: The turquoise green glazed lobster wall vase is a product of the Yongzheng period of the Qing Dynasty.

According to the relevant information, turquoise green glaze is a kind of imitation turquoise imitation stone glaze porcelain, which is a good monochrome glaze of Youzhen Fengchuang in the Yongzheng period of the Qing Dynasty.

1.Turquoise green glazed porcelain, showing blue-green, not pure green as we understand it today, a little yellowish, yellow with green; 2.Qing Dynasty turquoise green glazed porcelain was created in Yongzheng, Yongzheng did not have turquoise glazed porcelain before, if someone takes a Ming Dynasty turquoise green glazed porcelain, it is definitely not right, so this provides a theoretical basis for your appreciation; 3.

The turquoise glazed porcelain of Yongzheng and Qianlong is delicate, the glaze color is uniform, and there is a sense of uniformity and heaviness; 4.Qianlong turquoise green glaze ware is mostly small pieces of cultural toys and ornaments, and large pieces are rare, not that there are none; Pants this big 5After Jiaqing, the glaze of the turquoise grill was dark green, while the Yongzheng and Qianlong periods were relatively light.

Turquoise green glaze, also known as "okra green glaze", is a kind of porcelain glaze, which is a new variety of green glaze created in the Yongzheng period of the Qing Dynasty.

Modern formulas are formulated with barium sulfate, calcium carbonate, boric acid, etc. Its color is light yellow with a slight greenishness, which is similar to the color of turquoise, so it is called "turquoise green".

Turquoise green glaze is named because the glaze color resembles turquoise, and it is a new variety of monochrome glazed porcelain in the Qing Dynasty, which was created by Yongzheng. It uses the chemical element copper as the coloring agent, and is fired in an oxidizing atmosphere, which belongs to low-temperature glaze. Kang Yongqian three dynasties fired a lot of bionic porcelain, such as imitation wood glaze, imitation stone glaze, imitation carved lacquer glaze, imitation dried fresh fruits, imitation turquoise green glaze is one of them, its color and texture are very similar to natural turstone.