60si2mna tempering time

60si2mna spring steel60si2mna standard:gb/t 1222-2007

60Si2mna characteristics and scope of application:It is a widely used silicon-manganese spring steel with slightly higher strength, elasticity and hardenability than 55si2mn. It is suitable for the production of flat springs with large loads or coil springs with a wire diameter of less than 30mm in the railway vehicle and automobile tractor industry, and is also suitable for the production of heat-resistant springs in non-corrosive media with a working temperature of less than 250 and large and important coiled springs that bear alternating loads and work under high stress.

60Si2mna Chemical Composition:Carbon C:

Silicon si:manganese mn:

Sulfur s:

Phosphorus p:

Chromium cr:

Nickel ni:

Copper cu:

60si2mna delivery status:Hot-rolled steel is delivered in heat-treated or non-heat-treated condition, and cold-drawn steel is delivered in heat-treated condition.

60si2mna main specifications:60si2mna round bar, 60si2mna rolled bar, 60si2mna cold drawn bar, 60si2mna forging bar, 60si2mna plate, 60si2mna flat bar, 60si2mna forging, 60si2mna forging ring, 60si2mna machined parts, 60si2mna tube, 60si2mna forging cake.

150-200 tempering for 2-3 hours, 200-300 tempering hours, and more than 300 tempering for about 1 hour. Note that this material has 2 tempering brittleness, and it is necessary to avoid tempering in the tempering brittleness range.

60si2mn spring steel60si2mn standard:gb/t 1222-2007

60si2mn characteristics and scope of application:It is a widely used silicon-manganese spring steel with slightly higher strength, elasticity and hardenability than 55si2mn. It is suitable for the production of flat springs with large loads or coil springs with a wire diameter of less than 30mm in the railway vehicle and automobile tractor industry, and is also suitable for the production of heat-resistant springs in non-corrosive media with a working temperature of less than 250 and large and important coiled springs that bear alternating loads and work under high stress.

60Si2mn Chemical Composition:Carbon C:

Silicon si:manganese mn:

Sulfur s:

Phosphorus p:

Chromium cr:

Nickel ni:

Copper cu:

60si2mn Delivery Status:Hot-rolled steel is delivered in heat-treated or non-heat-treated condition, and cold-drawn steel is delivered in heat-treated condition.

60si2mn Main Specifications:60Si2Mn round bar, 60Si2mn rolled bar, 60Si2mn cold drawn bar, 60Si2mn forging bar, 60Si2mn plate, 60Si2mn flat bar, 60Si2mn forging, 60si2mn forging ring, 60si2mn machining parts, 60si2mn pipe, 60si2mn forging cake.

That's pretty much it, but it depends on how well you quench. The principles of temperature selection are: 1. The lower limit of tempering should be taken to pursue a high elastic limit; 2. The lower limit temperature should be taken for the surface ***, and the upper limit temperature should be taken otherwise.